Material scientists design damage-tolerant bone replacement
Our body is able to treat many injuries and wounds all by itself. Self-healing powers repair skin abrasions and enable bones to grow back together. However, doctors often have to lend a helping hand to repair bones after a fracture or due to a defect. Increasingly, bone replacement materials are being used, which partially or completely restore the form and function of the bone at the site of the damage. To ensure that such implants do not have to be replaced or repaired through extensive surgery in the event of damage, they should themselves possess self-healing capabilities. Material scientists at Friedrich Schiller University Jena have now developed a bone replacement material that minimises the extent of damage to it and at the same time repairs itself. They report on their research in the prominent research magazine "Scientific Reports".
Minimally invasive use of calcium phosphate cement
The experts from Jena, who collaborated with colleagues from the University of Würzburg as part of the German Research Foundation’s priority research programme "Self-healing Materials", concentrated on what is called calcium phosphate cement - a bone substitute that is already widely used in medicine. On the one hand, the material stimulates bone formation and increases the ingrowth of blood vessels. On the other hand, it can be introduced into the body as a paste in a minimally invasive procedure. There, its malleability allows it to bind closely to the bone structure.
"Due to its high degree of brittleness, however, cracks form in the material when it is subjected to excessive load. These cracks can quickly widen, destabilise the implant and ultimately destroy it - similar to concrete on buildings," explains Prof. Frank A. Müller from the University of Jena. "For this reason, calcium phosphate cement has so far mainly been used on bones that do not play a load-bearing role in the skeleton, for example in the mouth and jaw area."
Bridging and refilling cracks
The material scientists in Jena have now developed a calcium phosphate cement in which any cracks do not develop into catastrophic damage. Instead, the material itself seals them. The reason for this is carbon fibres that have been added to the material.
"Firstly, these fibres significantly increase the damage tolerance of the cement, because they bridge cracks as they form and thus prevent them from opening further," Müller explains. "Secondly, we have chemically activated the surface of the fibres. This means that as soon as the exposed fibres encounter body fluid, which collects in the openings created by the cracks, a mineralisation process is initiated. The resulting apatite - a fundamental building block of bone tissue - then closes the crack again."
The Jena scientists have simulated this process in their experiments by deliberately damaging the calcium phosphate cement and healing it in simulated body fluid. This intrinsic self-healing ability - and the greater load-bearing capacity associated with fibre reinforcement - could considerably expand the areas in which bone implants made of calcium phosphate cement can be used, which could possibly also include load-bearing areas of the skeleton in the future.